had been made to produce cast-steel without the use of a crucible—that is to say, on the 'open hearth' of the furnace. Reaumur was probably the first to show that steel could be made by fusing malleable iron with cast-iron. Heath patented the process in 1845; and a quantity of cast-steel was actually prepared in this way, on the bed of a reverberatory furnace, by Sudre, in France, during the year 1860. But the furnace was destroyed in the act; and it remained for Siemens, with his regenerative furnace, to realise the object. In 1862 Mr. Charles Atwood, of Tow Law, agreed to erect such a furnace, and give the process a fair trial; but although successful in producing the steel, he was afraid its temper was not satisfactory, and discontinued the experiment. Next year, however, Siemens, who was not to be disheartened, made another attempt with a large furnace erected at the Montlucon Works, in France, where he was assisted by the late M. le Chatellier, Inspecteur-Général des Mines. Some charges of steel were produced; but here again the roof of the furnace melted down, and the company which had undertaken the trials gave them up. The temperature required for the manufacture of the steel was higher than the melting point of most fire-bricks. Further endeavours also led to disappointments; but in the end the inventor was successful. He erected experimental works at Birmingham, and gradually matured his process until it was so far advanced that it could be trusted to the hands of others. Siemens used a mixture of cast-steel and iron ore to make the steel; but another manufacturer, M. Martin, of Sireuil, in France, developed the older plan of mixing the cast-iron with wrought-iron scrap. While Siemens was improving his means at Birmingham, Martin was obtaining satisfactory results with a regenerative furnace of his own